Quick Overview

Water and waste water treatment facilities

Primary and secondary containment structures

Tunnels and culverts

Dams, locks, canals, water reservoirs and aqueducts

Pipe penetrations

Swimming pools

Storage tanks

Retaining walls

Foundations

Slabs on grade

Interested in this item or want more information?

Phone:
Email: Sales@48ws.com

Can't find what you want? Give us a call and we can help you find it.

Details

Hydrotite is a state-of-the-art hydrophilic waterstop with unmatched durability and watersealing capacity. Comprised of Non-Bentonite, modified chloroprene rubber, Hydrotite expands up to EIGHT TIMES its original volume when exposed to water. This expansion creates an effective compression sealwithin joints of limited movement. Recognized worldwide, Hydrotite has a proven track record as a high quality and cost effective solution to your water containment needs. Leakmaster LV-1 is a single component water-swelling sealant with excellent and unique properties. Leakmaster may be applied in locations where conventional solid sealants cannot be easily applied.

Hydrotite Waterstop Physical Properties

Property Test Method Unit Hydrophilic Rubber Chloroprene Rubber

Minimum Typical Minimum Typical

Tensile Strength ASTM D412 lb/in2 350 366 1300 1570

Elongation ASTM D412 % 600 670 400 450

Hardness ASTM D2240 Shore A 52+/-5 54 50+/-5 50

Tear Resistance ASTM D624 lb/in 50 60.3 100 123

Specific Gravity ASTM D792 1.32+/-0.1 1.32 1.38+/-0.1 1.38

Leakmaster Physical Properties

General Properties

Appearance Putty-Like

Color Grey

Specific Gravity 1.30

Extrudability Within 20 seconds (at 23¡C)

Slump 3mm max. (at 23¡C)

Tack-Free Time Within 8 hours (at 23¡C, 60% R.H.)

JIS-A-5758

Properties AFTER HARDENING

Hardness 35 Shore A

Tensile Strength Tensile Strength

Elongation 1250%

Tear Strength 10 kgf/cm (56 lb/in)

JIS-K-6301

Adhesion Properties

Hardness Steel Aluminum Mortar

50% Modulus (kgf/cm2) 4.5 64 psi 6.5 92 psi 6.5 92 psi

Max. Tensile Strength (kgf/cm2) 7.0 99 psi 12.2 173 psi 11.1 157 psi

Elongation at Break (%) 330 580 570

Property	Test Method	Unit	Hydrophilic	Rubber	Chloroprene	Rubber
			Minimum	Typical	Minimum	Typical
Tensile Strength	ASTM D412	lb/in2	350	366	1300	1570
Elongation	ASTM D412	%	600	670	400	450
Hardness	ASTM D2240	Shore A	52+/-5	54	50+/-5	50
Tear Resistance	ASTM D624	lb/in	50	60.3	100	123
Specific Gravity	ASTM D792		1.32+/-0.1	1.32	1.38+/-0.1	1.38

Appearance	Putty-Like
Color	Grey
Specific Gravity	1.30
Extrudability	Within 20 seconds (at 23¡C)
Slump	3mm max. (at 23¡C)
Tack-Free Time	Within 8 hours (at 23¡C, 60% R.H.)
	JIS-A-5758

Hardness	35 Shore A
Tensile Strength	Tensile Strength
Elongation	1250%
Tear Strength	10 kgf/cm (56 lb/in)
	JIS-K-6301

Hardness	Steel	Aluminum	Mortar
50% Modulus (kgf/cm2)	4.5 64 psi	6.5 92 psi	6.5 92 psi
Max. Tensile Strength (kgf/cm2)	7.0 99 psi	12.2 173 psi	11.1 157 psi
Elongation at Break (%)	330	580	570

Additional Information

Manufacturer: Greenstreak